UNS N06600 Seamless Tube-pipe
UNS N06600 alloy is resistant to various corrosive media. The chromium composition gives the alloy better corrosion resistance under oxidation conditions than nickel 99.2(alloy 200) and nickel 99.2(alloy 201, low carbon). At the same time, the high nickel content makes the alloy have good corrosion resistance in reducing conditions and alkaline solution, and can effectively prevent the chlorine - iron stress corrosion cracking. Alloy 600 has good corrosion resistance in acetic acid, acetic acid, formic acid, stearic acid and other organic acids, and medium corrosion resistance in inorganic acids. High purity water used in primary and secondary cycles in nuclear reactors has excellent corrosion resistance. 600 in particular outstanding performance is able to resist dry chlorine gas and hydrogen chloride corrosion, application temperature up to 650℃. At high temperature, annealed and solution-treated alloys have good resistance to oxidation and high strength in air. The alloy is also resistant to ammonia and nitridizing and carburizing atmospheres, but when the REDOX conditions change alternately, the alloy will be subjected to partial oxidation medium corrosion (such as green death liquid).
Export Ireland UNS N06600 Seamless Tube- pipe
Specification: OD20*WT2*6000MM
Quantity: 700 pieces
Standard :ASTM B163
Weight: 4035kg
characteristic
1. It has good corrosion resistance to reduction, oxidation and nitriding media
2. It has good resistance to stress corrosion cracking at room temperature and high temperature
3. Good corrosion resistance to dry chlorine gas and hydrogen chloride gas
4. It has good mechanical properties at sub-zero, room temperature and high temperature
5. With good creep breaking strength, it is recommended to be used in the working environment above 700℃.
Application field
1. Erosive atmosphere of thermocouple casing
2. Production of vinyl chloride monomer: resistance to chlorine gas, hydrogen chloride, oxidation and carbonization corrosion
3. Conversion of uranium oxidation to hexafluoride: resistance to hydrogen fluoride corrosion
4. Areas of production and use of caustic alkali metals, particularly in the environment where sulfides are used
5. Titanium dioxide process with chlorine gas
6. Production of organic or inorganic chlorides and fluorides: resistance to chlorine and fluorine corrosion
7. Nuclear reactors
8. Curved neck bottles and components in heat treatment furnace, especially in carbonization and nitriding atmosphere
9. The catalytic regenerator in petrochemical production is recommended to use alloy 600 for longer service life in applications above 700℃.
NO6600 nickel alloy/nickel base alloy
·Monel400: Solid solution and high strength alloy over a wide temperature range for electronic components and springs. Corrosion and oxidation resistance at temperatures up to 1000ºF.
·Inconel600: High corrosion resistance, with excellent strength and easy machining characteristics. Mainly used in corrosive environment. It has chemical resistance at temperatures up to 2150ºF.
·Inconel 625: Excellent corrosion resistance and machinability. Suitable for temperatures from low temperatures to up to 2000ºF.
·Inconel718: High-strength, corrosion-resistant alloy for use in the nuclear industry at temperatures from 423ºF to 1300ºF.
·Inconel X750: precipitate-hardening nichcr alloy, strength for temperatures up to 1500ºF. Good corrosion resistance and oxidation resistance.
·Incoloy800: nickel, iron, chromium alloy, high temperature carburizing.
·Incoloy825: Alloy resistant to strong corrosion environment, such as liu acid, lin acid and seawater.
·Ni-Span-C902: nickel, iron, chromium alloy, suitable for the precise spring parts in the environment of drastic temperature change.
·Hastelloy C276: Suitable for chemical industry, resistant to yang chemical agent. Can replace HASTELLOY®C2, but with better machinability.
·Hastelloy X: jet engine components, including aftercombustion chambers, blades, liner, honeycomb, bellows and piping. Excellent strength and oxidation resistance at temperatures up to 2200ºF.
·Waspaloy: Main material for jet engine turbines, blades, spacers and shafts, suitable for high-temperature components.
Cobalt alloy/cobalt base alloy
·Haynes188: High strength and yang resistance at temperatures up to 2000°F, with excellent rear ductility.
·Haynes25: Also known as L605, jet engine component, combustion chamber and aftercombustion chamber component. In the environment of up to 1900ºF has yang chemical resistance and carburizing resistance, has a good high temperature strength.
·Nickel201: basically similar to Nickel200 except low carbon content to obtain better plasticity, mainly used in chemical industry.
·Hastelloy C-22: Nickel, chromium, molybdenum, tungsten alloy, corrosion resistance to many industrial chemicals, excellent weldability.
·Haynes214: precipitate-hardened nickel alloy with oxidation resistance up to 2000ºF. Used for furnace parts exposed to chromium carbon, chlorine pollution and chlorination environment and gas turbine parts.
·Haynes230: nickel, chromium, molybdenum, tungsten alloy, in the temperature of up to 2100ºF has excellent long-term yang resistance.